Teflon Suhu Tinggi Lembaran PTFE PTFE Lembaran Putih Dengan Grafit / Karbon / Perunggu Mengisi
1. intensitas tegangan Hti
2. tegangan tembus tinggi
3. suhu operasi yang lebih luas
Descriptio ns
Komponen yang dibuat dengan lembaran PTFE memiliki ketahanan yang luar biasa terhadap suhu tinggi serta suhu rendah, reaksi kimia, korosi, dan perengkahan tegangan. Sifat elektrik dan gesekan rendah PTFE membuatnya menjadi bahan pilihan untuk sejumlah aplikasi dan untuk teknik pemrosesan yang berbeda.
PTFE SHEET
|
ITEM
|
Result
|
Unit
|
|
Material
|
100% Virgin PTFE
|
|
|
Apparent density
|
2.10-2.30
|
g/ cm3
|
|
Tensile Strength
|
22-28
|
Mpa
|
|
Ultimate Elongation
|
250-300
|
%
|
|
Dielectric Strength
|
40
|
KV/mm
|
|
Tempature Resist
|
-180-+260
|
oC
|
|
PTFE Molded sheet Thickness
|
1.5mm-----120mm
|
|
Molded sheet
Length * width
|
Min Dimension=300x300mm, Max Dimension= 2000x2000mm Other sizes based on your requirements
|
|
PTFE Skived sheet thickness
|
0.1mm-----10.0mm
|
|
PTFE Skived sheet width(Max)
|
2700mm
|
Fitur utama
1. properti resistensi Panas --- Itu mampu wajan stabil antara -180 ° C sampai + 260 ° C.
2. Properti non-lengket yang sangat baik --- Lebih mudah untuk menghilangkan resin, dopes, minyak dan benda lengket lainnya.
3. Properti mekanik yang baik tanpa distorsi dan koefisien gesekan rendah.
4. properti isolasi Yang Sangat Baik.
5. Bahan seperti karbon, grafit dan serat kaca dapat diisi.
6.Virgin dan bahan daur ulang tersedia
Properti utama
|
Properties
|
Unit
|
Result
|
|
Apparent density
|
g/cm3
|
2.10-2.20
|
|
Tensile strength (min)
|
MPa
|
20
|
|
Ultimate elongation (min)
|
%
|
200
|
|
Residual Lubricant Content (max)
|
%
|
0.5
|
|
Dialectric Strength (min)
|
KV/mm
|
10
|
Gambar:
Detail:
PTFE resin, diisi dengan beberapa barang mengisi, dapat memperpanjang umur produk
dan memperkuat kinerja, misalnya: Grafit, Karbon, serat kaca, perunggu
|
Glass Fiber:
|
Increases compressive strength, rigidity and wear.
Reduces creep and cold flow
Minimal effect on chemical and electrical properties
|
|
Carbon:
|
Increases compressive strength, hardness, wear, and load properties.
Good chemical resistance
Various types and amounts of carbon can be added to alter conductivity
|
|
Graphite:
|
Reduces coefficient of friction
Reduces initial wear
Increases strength
|
|
Molybdenum Disulfide:
|
Increases hardness, stiffness, and wear
Minimal effect on chemical and electrical properties
|
|
Bronze:
|
Increases hardness and wear resistance
Increases dimensional stability and compressive strength
Not suitable for corrosive or electrical applications
|
Aplikasi:
1. Menempel menempel pada pemanasan hingga datar untuk mengurangi gesekan .
2. Digunakan dalam membungkus kabel di bawah tegangan tinggi dan suhu tinggi.
3. Digunakan untuk menyegel bagian elektronik.
Kategori Produk : Produk PTFE > Lembar PTFE